Waste tarpaulin fiber as an additive in concrete /
Cordero, Ace Eldrin T.
Waste tarpaulin fiber as an additive in concrete / by Ace Eldrin T. Cordero and Jose Marie M. De Grano. - Indang, Cavite : Cavite State University- Main Campus, 2019. - xxiv, 138 pages : illustrations ; 28 cm.
Thesis (Bachelor of Science in Civil Engineering) Cavite State University.
Includes bibliographical references.
College of Engineering and Information Technology (CEIT), Department of Civil Engineering College of Engineering and Information Technology (CEIT), Department of Civil Engineering
CORDERO, ACE ELDRIN T. And DE GRANO, JOSE MARIE M. Waste Tarpaulin Fiber as an additive in concrete. Undergraduate Thesis. Bachelor of Science in Civil Engineering. Cavite State University, Indang, Cavite. June 2019. Adviser: Engr. Cene M. Bago.
Tarpaulin Fiber is considered as possible reinforcement material that has different properties. However, tarpaulins were just dumped after using in different events that considered as waste material. The best way to lessen that problem is to develop the usage of waste tarpaulin as a resource material. The main objective of the study was to determine the effect of waste tarpaulin fiber on the flexural and compressive strength of fiber reinforced concrete.
In this study waste tarpaulin is used as an additive in concrete. The cost of producing tarpaulin fiber as an additive in concrete is compared with the plain concrete. The Highest strength of tarpaulin fiber was observed from a single strand of 10inch diameter of tarpaulin fiber that held 883.3 grams before rupture. The researchers observed that the fiber did not absorbed water.
Four treatments were conducted (0%, 15%, 20%, and 25%) and the results revealed that the treatment with 20% gained the highest compressive and flexural strength, while the treatment without the tarpaulin fiber obtained the least strength. Waste Tarpaulin fiber as an additive in concrete gained a good result of adding strength in compressive and flexural strength in concrete. Since the effect of adding tarpaulin fiber in concrete occurred when the amount of fibers are moderate, future researchers are encouraged to evaluate higher percentage of fiber to know the effects in concrete for both compressive and flexural strength.
The researchers used Class A mixture design in this study, future researchers are encouraged to use different mixture design to evaluate the effects of adding tarpaulin fiber in concrete. It can be utilized the behavior of tarpaulin fiber in different construction materials like bricks and pavement.
Recycling
Waste products as building materials
628.445 / C81 2019
Waste tarpaulin fiber as an additive in concrete / by Ace Eldrin T. Cordero and Jose Marie M. De Grano. - Indang, Cavite : Cavite State University- Main Campus, 2019. - xxiv, 138 pages : illustrations ; 28 cm.
Thesis (Bachelor of Science in Civil Engineering) Cavite State University.
Includes bibliographical references.
College of Engineering and Information Technology (CEIT), Department of Civil Engineering College of Engineering and Information Technology (CEIT), Department of Civil Engineering
CORDERO, ACE ELDRIN T. And DE GRANO, JOSE MARIE M. Waste Tarpaulin Fiber as an additive in concrete. Undergraduate Thesis. Bachelor of Science in Civil Engineering. Cavite State University, Indang, Cavite. June 2019. Adviser: Engr. Cene M. Bago.
Tarpaulin Fiber is considered as possible reinforcement material that has different properties. However, tarpaulins were just dumped after using in different events that considered as waste material. The best way to lessen that problem is to develop the usage of waste tarpaulin as a resource material. The main objective of the study was to determine the effect of waste tarpaulin fiber on the flexural and compressive strength of fiber reinforced concrete.
In this study waste tarpaulin is used as an additive in concrete. The cost of producing tarpaulin fiber as an additive in concrete is compared with the plain concrete. The Highest strength of tarpaulin fiber was observed from a single strand of 10inch diameter of tarpaulin fiber that held 883.3 grams before rupture. The researchers observed that the fiber did not absorbed water.
Four treatments were conducted (0%, 15%, 20%, and 25%) and the results revealed that the treatment with 20% gained the highest compressive and flexural strength, while the treatment without the tarpaulin fiber obtained the least strength. Waste Tarpaulin fiber as an additive in concrete gained a good result of adding strength in compressive and flexural strength in concrete. Since the effect of adding tarpaulin fiber in concrete occurred when the amount of fibers are moderate, future researchers are encouraged to evaluate higher percentage of fiber to know the effects in concrete for both compressive and flexural strength.
The researchers used Class A mixture design in this study, future researchers are encouraged to use different mixture design to evaluate the effects of adding tarpaulin fiber in concrete. It can be utilized the behavior of tarpaulin fiber in different construction materials like bricks and pavement.